Pegboard

Why Choose Evowood Pegboard?

Extra Strong
Evowood Pegboard boasts a much higher tensile strength, structural strength and internal bond than other subtitutes on the market (MDF & HDF). It is also durable, resistant to abrasions and will not split, splinter or crack.

Anti Warp
Evowood Pegboard is denser than other thin boards substitutes on the market (MDF & HDF), making it less prone to warping while still remaining lightweight.

Easy Wipe
Evowood Pegboard is easy to clean. Simply use mild soapy water to remove dust and dirt from the surface of the hardboard. Evowood Pegboard also has a smooth surface for paint finishes.

Supa-Flex
Inherently flexible without compromising on durability. Evosure Pegboard can be easily bent and curved into shape as necessary, making it suitable for variety of applications.

Versatile
Able to be used to for a wide range of applications, Evowood Pegboard is the ideal material for a variety of storage and design solutions in the home or business.

Green
Our products are formaldehyde free, carry an e-zero emission rating and are manufactured in accordance with FSC™ regulations using natural binders.

Clear

Evowood Pegboard

Anti-warp, Easy-Wipe, Extremely Versatile

Our Pegboard range can be used for applications such as:

Storage Solutions

Workshop Storage

Kitchen Storage

Shop Fitting

Exhibition Displays

Decor Arrangements

Materials Data

Pegboard is available in a wide range of sizes. See the table below for a full list of materials data.

PropertyUnitSpecification
Nominal Thicknessmm3.2
Thickness Tolerancemm +/-0.4
Masskg/m³ approx3.2
Densitykg/m³ max940
Linear Expansion/Contraction in Range 33% to 90% RH @20ºC%0.25
Thermal Conductivity (k)W/MºC Av0.12
Thermal Resistance (R)M2ºC/W Av0.227
Bending Strength (M.O.R.)
Modular of Rupture
MPa min38
Internal Bond StrengthMPa min0.7
Shear ResistanceMPa Av35
Lateral Nail Holding Ability (using a 3mm diameter pin)N/mm Thick min120
Water Absorption After 24 Hrs
Immersion at 20ºC
% max30
Thickness Increase After 24 Hrs in Water at 20ºC% max18
Thickness Increase from 33% to 90% RH at 20ºC% max7